Type:
Journal
Description:
Stacked aluminum oxide/aluminum nitride (Al2O3/AlN) layers were deposited on n-type (0001) 4H–SiC by atomic layer deposition (ALD) processes. The structural and chemical properties have been investigated and are consistent with the growth of ∼9 nm oriented (0001) AlN layer, and an upper 20 nm amorphous Al2O3 layer. The entire Al2O3/AlN stack was electrically characterized and compared with respect to a single Al2O3 layer having the same total thickness. The Al2O3/AlN bilayer exhibited a higher dielectric constant (κ = 8.7), a significant reduction of the oxide trapped charges (NOT) from 7.8 × 1012 to 1.8 × 1012 cm−2, as well as a decrease of a factor 2 of the interface traps density (Dit) compared with the Al2O3 single layer values. A large positive flat band voltage shift was observed in the C–V curves acquired on MIS capacitors. The comparison of the behaviour of MIS capacitors fabricated on both n …
Publisher:
Pergamon
Publication date:
1 May 2024
Biblio References:
Volume: 174 Pages: 108244
Origin:
Materials Science in Semiconductor Processing